#71 Aluminum Brazing Flux
The thorough cleaning action of this flux
ensures quick melting and easy spreading of the filler metal.
Prevents formation of oxides at the brazing temperature,
allowing deep penetration of the rod metal, for a strong,
smooth joint.* Recommended for use with #718 Aluminum
Brazing Rods.
Use dry or make a paste. Apply to cleaned metal;
apply heat, when flux flows apply brazing rod.**
Meets Mil Spec: 3412-A
Working Range: Approximately 915° - 1115° F
AWS Classification: Type l
Sizes: 1/4 lb - 1/2 lb - 1 lb
*Used for aluminum and aluminum alloys at temperatures
of 1050° F and above.
**Designed specifically for torch and furnace
brazing operations.
#73 Aluminum Welding Flux
Use for welding aluminum and alloys. Recommended for
use with #4043 Bare Aluminum. This flux produces a strong,
non-porous weld by keeping the base metal and rod free of
oxides during welding. Mix with water to form a paste and
apply to both rod and metal. After welding, remove residue
with warm water. Basically use the same as #71 except that
heat is applied to base metal.
Melting Point: Approximately 1100° F
Sizes: 1/4 lb - 1/2 lb - 1 lb
#75 Magnesium Welding Flux
The active fluxing agent removes the oxides and impurities
permitting free flow of the filler metal. Mix with water
to form a paste and apply to both rod and base metal.
After welding, remove residue with warm water.
Meets Mill Spec: F6943-B
Working Range: 900° - 1150° F
Sizes: 1/4 lb - 1/2 lb - 1 lb
Standard Packaging:
6 @ 1/4# jars per box
6 @ 1/2# jars per box
4 @ 1# jars per box
#585 Super Soldering Flux
A paste soldering flux used for high temperature soldering
of aluminum and zinc die cast alloy. Used with Aladdin #33
Low Melt Aluminum solder to join aluminum to copper, steel,
brass, galvanized metal, stainless steel and monel metals.
Also recommended for use with 50/50 tin-lead and 95/5
zinc-aluminum solder. Produces especially tight joints
when soldering copper to aluminum.
Meets Mil Spec: O-F-499c, Type B
Working Range: 670° - 720°F
By Weight: 1/2 lb
Flammable Liquid / Corrosive Liquid N.O.S. Propyl
Alcohol and Zinc Chloride UN 2924
#96 Silver Brazing Flux
A superior general all-purpose silver brazing flux for
all silver alloys, with excellent creep and flowability.
Designed for use with copper, brass, bronze, cast iron,
monel, nickel, refractories, steel and stainless steel
applications. Commonly used in torch, furnace, and
induction applications. Residue easily removed with water
while the joint is hot.
Meets Mil Spec: O-F-499c,Type B
Working Range: 1050° - 1600° F
AWS Classification: Type 3-4
By Weight: 1/4 lb - 1/2 lb - 1 lb
#255 Non-Corrosive Soldering Paste
Always sure and ready to use. (Petroleum base) Excellent
all purpose soldering paste flux. Put on a little
paste - then solder.
Mil Spec: O-F-506c, Type I Form A
Sizes: 2 oz Tin - 12 per box
4 oz Tin - 1 lb Tub - 5 lb Tub
#621 Solder Salts
Excellent brazing flux in crystalline form. Concentrated
dry flux blend. Just add water to make your own brazing
flux. Widely used in radiator repair. Can be used on
most metals.
Sizes: 1 lb can
Watch for our new
BRONZE FLUX –
coming soon!
|
|
 |
|
|